Abstract Electrochemical two-electron water oxidation reaction (2e-WOR) has drawn significant attention as a promising process to achieve the continuous on-site production of hydrogen peroxide (H₂O₂). However, compared to the cathodic H₂O₂generation, the anodic 2e-WOR is more challenging to establish catalysts due to the severe oxidizing environment. In this study, we combine density functional theory (DFT) calculations with experiments to discover a stable and efficient perovskite catalyst for the anodic 2e-WOR. Our theoretical screening efforts identify LaAlO₃perovskite as a stable, active, and selective candidate for catalyzing 2e-WOR. Our experimental results verify that LaAlO₃achieves an overpotential of 510 mV at 10 mA cm⁻²in 4 M K₂CO₃/KHCO₃, lower than those of many reported metal oxide catalysts. In addition, LaAlO₃maintains a stable H₂O₂Faradaic efficiency with only a 3% decrease after 3 h at 2.7 V vs. RHE. This computation-experiment synergistic approach introduces another effective direction to discover promising catalysts for the harsh anodic 2e-WOR towards H₂O₂. 

Electrochemical oxidation of water and electrolyte ions is a sustainable method for producing energy carriers and valuable chemicals. Among known materials for catalyzing oxidation reactions, titanium dioxide (TiO 2 ) offers excellent electrochemical stability but is less active than many other metal oxides. Herein, we used density functional theory calculations to predict an increase in catalytic activity by doping anatase TiO 2 with manganese atoms (Mn). We synthesized Mn-doped TiO 2 and then utilized X-ray absorption spectroscopy to study the chemical environment around the Mn site in the TiO 2 crystal structure. Our electrochemical experiments confirmed that TiO 2 , with the optimal amount of Mn, reduces the onset potential by 260 mV in a 2 M KHCO 3 (pH = ∼8) electrolyte and 370 mV in a 0.5 M H 2 SO 4 (pH = ∼0.5) electrolyte. Moreover, in 0.5 M H 2 SO 4 , we observed that the amount of Mn doping greatly impacts the selectivity towards oxygen production versus peroxysulfate formation. In 2 M KHCO 3 , the Mn doping of TiO 2 slightly decreases the selectivity towards oxygen production and increases the hydrogen peroxide formation. The Mn-doped TiO 2 shows good electrochemical stability for over 24 hours in both electrolytes.